Overview of chromium carbide Cr3C2 powder
Chromium carbide is an organic compound with a molecular formula of Cr3C2 and a molecular weight of 180.01. Gray powder, orthorhombic system, a=2.821, b=5.52, c=11.46, melting point 1890℃, boiling point 3800℃. Micro Vickers hardness (load 50g) is 2700kg/rnrn2, thermal expansion coefficient is 10.3×10-6/K, insoluble in water, acid and alkali resistant, is a high melting point inorganic material, good wear resistance, in high temperature environment (1000-1100 degrees) Corrosion and oxidation resistance.
The production process of chromium carbide
Metal chromium powder carbonization method: carbon black and electrolytic chromium are crushed into 325 mesh metal chromium powder according to the ratio of 13.5% to 64% (mass) (exceeding the theoretical combined carbon content of 11.33%). After dry mixing with ball mill as raw material. Add 1% to 3% stearic acid as a molding lubricant. 1T/cChemicalbookm2 or more pressure compression molding. Put the pressed powder into a graphite plate or crucible, heat it to 1500-1700°C (the dew point of hydrogen is about -35°C) with a Taman furnace or an induction heating furnace in a hydrogen stream, and then keep it for 1 h to make the chromium A carbonization reaction occurs to form chromium carbide, which is cooled to obtain chromium carbide.
How is chromium carbide Cr3C2 powder produced?
Chromium carbide is produced by a combination of aluminothermic reduction and vacuum furnaces at temperatures of 1500°C and above. A mixture of chromium metal, chromium oxide and carbon is prepared and charged into a vacuum furnace. The pressure in the furnace decreased and the temperature rose to 1500°C. The carbon reacts with the chromium oxide to form chromium metal and carbon monoxide gas, which is pumped into a vacuum pump. The chromium metal then combines with the remaining carbon to form chromium carbide.
The precise balance between chromium oxide, chromium metal and carbon determines the grade of chromium carbide produced. This is strictly controlled to ensure product quality suitable for demanding markets such as aerospace.
Chromium carbide Cr3C2 powder application
Chromium carbide Cr3C2 powder is a high melting point material with good wear resistance, corrosion resistance and oxidation resistance in high temperature environment. Made of nichrome carbide particles, plasma sprayed for high temperature and wear resistance.
1. Anti-oxidation, anti-oxidation and acid-resistant coatings are widely used in aero-engines and petrochemical machinery and equipment, which can greatly improve the service life of machinery. It is also commonly used as a grain refiner for cemented carbide and cemented carbide. Other wear-resistant and corrosion-resistant parts. Cr3C2-based cermets have excellent oxidation resistance at high temperatures.
2. For chromium carbide ceramics. Coarse chromium carbide is used as a melt-blown material to form a melt-blown layer on the surface of metals and ceramics, thereby endowing ceramics with wear resistance, heat resistance, corrosion resistance and other properties. It is widely used in aircraft engines and petrochemical machinery, greatly extending the service life of the machinery. Also used for spraying semiconductor films.
3. As a thermal spray material, chromium carbide Cr3C2 powder is used to protect the underlying metal surface.
4. Additives for the manufacture of wear-resistant and corrosion-resistant materials.
5. As a coating for seals, bearings and valve seals.
6. As a microcrystalline phase in cemented carbide (such as vanadium carbide), chromium carbide Cr3C2 powder is used to inhibit the growth of submicron grains during pressing and sintering.
Chromium carbide Cr3C2 powder price
The price of chromium carbide Cr3C2 powder will change with the production cost, transportation cost and the international situation. The market supply and demand of chromium carbide Cr3C2 powder varies randomly. Tanki New Materials Co.,Ltd aims to help various industries and chemical wholesalers find high-quality, low-cost nanomaterials and chemicals by providing a full range of customized services. If you are looking for Chromium Carbide Cr3C2 Powder, please feel free to send an inquiry to get the latest price of Chromium Carbide Cr3C2 Powder.
Chromium carbide Cr3C2 powder suppliers
As a global supplier of chromium carbide Cr3C2 powders, Tanki New Materials Ltd. has extensive experience in the performance, application and cost-effective manufacturing of advanced and engineered materials. The company has successfully developed a series of powder materials (including boron carbide, aluminum carbide, titanium carbide, etc.), high-purity target materials, ceramics and structural devices, and provides OEM services.
|Technical Parameter of Chromium Carbide Cr3C2 Powder :|
|Total C||Free C||O||N||Fe||Ca||Si||Mo||Al||Na|
|Chromium Carbide Properties|
|Other Names||chrome carbide, chromic carbide, trichromium dicarbide,|
|chromium carbon, Cr3C2 powder|
|Appearance||Gray to Black Powder|
|Melting Point||1895 °C|
|Solubility in H2O||N/A|
|Chromium Carbide Health & Safety Information|
Chromium carbide powder is a high melting point inorganic material with good wear resistance,It is used as a thermal spray material for metal surface protection and is also often used as hard alloy.…
Iron oxide Fe3O4 powder, commonly known as black iron oxide, magnetite and black iron oxide, is used in many different fields, it is commonly used as a pigment and polish, and in the manufacture of audio cassettes and telecommunications equipment.…
Vanadium nitride is known as VN powder, it is an important vanadium alloy additive, and vanadium nitride is used in lithium electronic batteries and energy storage materials.…